OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts

JimaFor
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now
    Buy cheap OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts from wholesalers
     
    Buy cheap OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts from wholesalers
    • Buy cheap OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts from wholesalers
    • Buy cheap OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts from wholesalers
    • Buy cheap OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts from wholesalers
    • Buy cheap OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts from wholesalers

    OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts

    Ask Lasest Price
    Brand Name : JIMA
    Model Number : ALP
    Certification : ISO9001-2008,SGS,ROHS.
    Price : Negotiations
    Payment Terms : T/T, L/C
    Supply Ability : 10000 pcs /per month
    Delivery Time : 15~30days
    • Product Details
    • Company Profile

    OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts


    OEM 7079 Forging Aluminum Parts For Skeleton Large Forgings/Spare Parts/Die Forged


    Product Details


    Material

    Aluminum Alloy 7079

    Process

    Forging+CNC+Heat Treatment

    Surface Treatment

    Transparent, Color Anodized, Hard Anodizing, Powder Coating;
    Sandblasting, Laser Carving, Silk Screening;
    Nickel-Plated, Chrome, Galvanized, Silver/Gold Plating;
    Black Oxide Coating, Polishing; etc...

    Manufacture Ability

    Depends on The Complexity Of Different Products And Quantities

    Experience

    Aluminum Machining Service for 12 Years

    Packaging

    Standard Export Wooden Pallets
    Another Request According to Your Needs

    MOQ

    1pcs

    Sample

    Can Be Customized

    Mold

    Can Be Customized

    Lead Time

    Mold for 15-20 Days

    Process for 15-20 Days

    OEM

    Can Be Customized


    Chemical Composition of 7079

    Alloy

    Si

    Fe

    Cu

    Mn

    Mg

    Cr

    Zn

    Ti

    Others

    Al

    Each

    Total

    7079

    0.30max

    0.40max

    0.40-0.80

    0.10-0.30

    2.90-3.70

    0.10-0.25

    3.80-4.80

    0.10max

    0.05max

    0.15max

    Rest


    Technical Specifications of 7079


    7079 Aluminum Mechanical Properties


    Hardness, Brinell

    150

    150

    AA; Typical; 500 g load; 10 mm ball

    Hardness, Knoop

    191

    191

    Converted from Brinell Hardness Value

    Hardness, Rockwell A

    53.5

    53.5

    Converted from Brinell Hardness Value

    Hardness, Rockwell B

    87

    87

    Converted from Brinell Hardness Value

    Hardness, Vickers

    175

    175

    Converted from Brinell Hardness Value

    Ultimate Tensile Strength

    572 MPa

    83000 psi

    AA; Typical

    Tensile Yield Strength

    503 MPa

    73000 psi

    AA; Typical

    Elongation at Break

    11 %

    11 %

    AA; Typical; 1/16 in. (1.6 mm) Thickness

    Elongation at Break

    11 %

    11 %

    AA; Typical; 1/2 in. (12.7 mm) Diameter

    Modulus of Elasticity

    71.7 GPa

    10400 ksi

    AA; Typical; Average of tension and compression. The compression modulus is about 2% greater than tensile modulus.

    Poisson’s Ratio

    0.33

    0.33


    Fatigue Strength

    159 MPa

    23000 psi

    AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen

    Fracture Toughness

    20 MPa-m½

    18.2 ksi-in½

    K(IC) in S-L Direction

    Fracture Toughness

    25 MPa-m½

    22.8 ksi-in½

    K(IC) in T-L Direction

    Fracture Toughness

    29 MPa-m½

    26.4 ksi-in½

    K(IC) in L-T Direction

    Machinability

    70 %

    70 %

    0-100 Scale of Aluminum Alloys

    Shear Modulus

    26.9 GPa

    3900 ksi


    Shear Strength

    331 MPa

    48000 psi

    AA; Typical


    7079 Aluminum Thermal Properties

    CTE, linear 68°F

    23.6 µm/m-°C

    13.1 µin/in-°F

    AA; Typical; Average over 68-212°F range.

    CTE, linear 250°C

    25.2 µm/m-°C

    14 µin/in-°F

    Average over the range 20-300ºC

    Specific Heat Capacity

    0.96 J/g-°C

    0.229 BTU/lb-°F


    Thermal Conductivity

    130 W/m-K

    900 BTU-in/hr-ft²-°F

    AA; Typical at 77°F

    Melting Point

    477 – 635 °C

    890 – 1175 °F

    AA; Typical range based on typical composition for wrought products 1/4 inch thickness or more significant. Homogenization may raise the eutectic melting temperature by 20-40°F but usually does not eliminate eutectic melting.

    Solidus

    477 °C

    890 °F

    AA; Typical

    Liquidus

    635 °C

    1175 °F

    AA; Typical


    Product Show




    Quality OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts for sale
    Inquiry Cart 0
    Send your message to this supplier
     
    *From:
    *To: JimaFor
    *Subject:
    *Message:
    Characters Remaining: (0/3000)